600mm daya dhuwur grafit elektroda
Kelas: Dhuwur Daya
Tungku sing ditrapake: EAF
Dawane: 2100mm / 2400mm / 2700mm
Puting: 3TPI/4TPI
Pembayaran: T / T, L / C
Istilah Pengiriman: EXW / FOB / CIF
MOQ: 10 ton
| Perbandingan Spesifikasi Teknis HP Graphite Electrode 24″ | ||
| Elektroda | ||
| Item | Unit | Spesifikasi Supplier |
| Ciri khas Kutub | ||
| Diameter nominal | mm | 600 |
| Diameter Max | mm | 613 |
| Diameter Min | mm | 607 |
| Panjang Nominal | mm | 2200-2700 |
| Max Length | mm | 2300-2800 |
| Min Length | mm | 2100-2600 |
| Kapadhetan Bulk | g/cm3 | 1.68-1.72 |
| kekuatan transversal | MPa | ≥10.0 |
| Modulus Muda | GPa | ≤12.0 |
| Resistance spesifik | µΩm | 5.2-6.5 |
| Kapadhetan saiki maksimum | KA/cm2 | 13-21 |
| Kapasitas Ngangkut Saiki | A | 38000-58000 |
| (CTE) | 10-6 ℃ | ≤2.0 |
| kandungan abu | % | ≤0.2 |
| Karakteristik Khas Puting (4TPI/3TPI) | ||
| Kapadhetan Bulk | g/cm3 | 1.78-1.83 |
| kekuatan transversal | MPa | ≥22.0 |
| Modulus Muda | GPa | ≤15.0 |
| Resistance spesifik | µΩm | 3.2-4.3 |
| (CTE) | 10-6 ℃ | ≤1.8 |
| kandungan abu | % | ≤0.2 |
Dibandhingake karo tembaga, grafit nduweni kaluwihan kayata konsumsi kurang, tingkat discharge luwih cepet, bobot entheng lan koefisien expansion termal cilik, supaya mboko sithik ngganteni elektroda tembaga dadi bahan utama Processing discharge. Miturut kapasitas tungku listrik, elektroda grafit kanthi diameter beda digunakake. Kanggo nggunakake terus-terusan saka elektrods, elektrods disambungake dening sambungan Utas saka elektrods. Elektroda grafit sing digunakake ing nggawe baja kira-kira 70-80% saka total konsumsi elektroda grafit.
Konsumsi elektroda grafit lan rusak umum ing praktik. Apa sing nyebabake iki? Punika analisis kanggo referensi.
| Faktor | Rusak awak | Pecah Puting | Loosening | Spalling | Electtode Mundhut | Oksidasi | Konsumsi Electorde |
| Non-konduktor sing tanggung jawab | ◆ | ◆ |
|
|
|
|
|
| Kethokan abot sing tanggung jawab | ◆ | ◆ |
|
|
|
|
|
| Transformer overcapacity | ◆ | ◆ |
| ◆ | ◆ | ◆ | ◆ |
| Ketidakseimbangan telung fase | ◆ | ◆ |
| ◆ | ◆ |
| ◆ |
| Rotasi Fase |
| ◆ | ◆ |
|
|
|
|
| Geter banget | ◆ | ◆ | ◆ |
|
|
|
|
| Tekanan Clamper | ◆ |
| ◆ |
|
|
|
|
| Soket elektroda atap ora sejajar karo elektroda | ◆ | ◆ |
|
|
|
|
|
| Cooling banyu disemprot ing elektroda ndhuwur gendheng |
|
|
|
|
|
| △ |
| Scrap preheating |
|
|
|
|
|
| △ |
| Tegangan sekunder dhuwur banget | ◆ | ◆ |
| ◆ | ◆ |
| ◆ |
| Arus sekunder dhuwur banget | ◆ | ◆ |
| ◆ | ◆ | ◆ | ◆ |
| Daya kurang banget | ◆ | ◆ |
| ◆ | ◆ |
| ◆ |
| Konsumsi lenga dhuwur banget |
|
|
| ◆ | ◆ |
| ◆ |
| Konsumsi oksigen dhuwur banget |
|
|
| ◆ | ◆ |
| ◆ |
| pemanasan dawa |
|
|
|
|
|
| ◆ |
| Elektroda dipping |
|
|
|
| ◆ |
| ◆ |
| Bagian sambungan sing reged |
| ◆ | ◆ |
|
|
|
|
| Pangopènan sing ora apik kanggo colokan angkat lan alat pengencang |
| ◆ | ◆ |
|
|
|
|
| Sambungan ora cukup |
| ◆ | ◆ |
|
|
|
|
◆ Sing dadi faktor apik
△ Singkatan saka faktor sing ora apik